Description
SIKA® FILLER-101 | FINE SURFACE FILLER
Premium, fine surface filler
Very fine consistency for fine surface filling
Application thickness up to 3mm per layer
Fast drying and easy to sand
USE
Suitable for indoor filling work on plaster boards, fabrics, old wallpapers, etc.
Smooth finish
CHARACTERISTICS AND ADVANTAGES
Ready to use, no mixing required
Easy application
High initial tack or grab on plaster and concrete
Quick drying
COLOUR: White
Appearance / Colour White paste
Packaging 500 ml plastic tube
Storage
Storage Conditions / Shelf-Life
12 months from date of production if stored properly in undamaged and unopened original sealed packaging, in cool and dry conditions. Protect from frost.
Technical Data
Chemical Base Filled styrene-acrylate dispersion.
Density ~ 1.100 kg/l
Solid Content
~ 55%
Grading Dmax : 0.12 mm
Layer Thickness 3 mm max.
Application Details
Consumption
This depends on the substrate roughness and thickness of the layer applied.
As a guide, ~ 1 l of Sika®
Filler-101 can fill ~ 1 m2 per mm thick.
Substrate Quality Clean, free from dust, dry and oil.
Application
Conditions / Limitations
Substrate Temperature +5°C min. / +35°C max.
Ambient Temperature +5°C min. / +35°C max.
Application Instructions
Mixing Sika® Filler-101 is supplied ready to use - no mixing is required.
Application Method / Tools
Sika® Filler-101 can be applied with spatula in layer thicknesses from 0 - 3 mm. When filling deeper holes or cracks the filler must be applied in several layers and must be allowed to almost dry. Holes and cracks from 4 - 15 mm can more easily be filled with Sika® Filler-105. When dried finish the surface with Sika® Filler-101. Cleaning of Tools Clean all tools and application equipment with water immediately after use. Hardened / cured material can only be mechanically removed.
Waiting Time / Overcoating
Drying Time: ~ 2 hours
Paintability: ~ 4 hours
Value Base All technical data stated in this Product Data Sheet are based on laboratory tests.
Actual measured data may vary due to circumstances beyond our control.